Hot Rolled Carbon Steel Coils SS400 Q235b A36 Ms Steel Plate Coil
| Strip steel is non-shrinking and non-creeping at ambient temperatures. It is a uniform, lightweight steel that is easy to fabricate, transport, and install. While it's available in a variety of tempers, determining the proper temper for your project depends on your formability needs. |
Product Description:
| Materials | Carbon Steel Sheet Coil |
| Standard | GB,JIS(or as customer's requirement) |
| Size: | Width:600-1250mm |
| | Thickness:0.12—2mm |
| General Width | 910mm, 1010mm, 1219mm,1220mm,1250mm,1500mm |
| Tolerance | Thickness: +/-0.02mm Width:+/-2mm |
| Workflow | Hot rolled coil–Pickling – Cold rolling – Cover annealing –Skin pass – Coiling |
| Package | Seaworthy packing. Or as customer’s request. |
| Production Capacity | 50000 Tons per Month |
| Loading | Per container can be loaded 25 tons to 27 tons. |
| Port of shipment | China port |
| Payment | TT or 100% Irrevocable L/C at sight |
| Delivery time | 10--30days after receiving customer’s deposit or L/C. |
| Application | Automobile making, Electrical appliance, Locomotive and car, airlines, precision meter, Canned food packing, etc. |
| Price Term | FOB/CFR/CIF |
Chemical Composition
| Specification | Grade | Chemical Composition(wt%) |
| C | Mn | Ni | Cr | Mo | Ti |
| ASTMJIS | 316L/022Cr17Ni12Mo2 | ≤0.03 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | - |
| JIS | SUS316L | ≤0.03 | ≤2.0 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 | - |
| ASTMJIS | 316Ti/SUS 316Ti | ≤0.08 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | 5*(C+N)-0.7 |
Properties
| Spec | Grade | Mechanical Property | Physical Property |
| Y.S (N/MM2) | T.S (N/MM2) | EL (%) | HRB | Specific Heat (J/g℃) | Modulus of Elasticity (KN/mm2) |
| ASTM/GB | 316L/022Cr17Ni12Mo2 | ≥170 | ≥485 | ≥40 | ≤95 | 0.5 | 193 |
| JIS | SUS316L | ≥175 | ≥480 | ≥40 | ≤90 | 193 |
| ASTM | 316Ti | ≥205 | ≥515 | ≥40 | ≤95 | 0.5 | 200 |
Applications: 316L: Widely used in corrosion-susceptible environment and some mechanical components those are difficult to make heat treatment after forming in more corrosive environment. 316Ti: Mainly used for industrial components. |